CeAgAs2 - a New Derivative of the HfCuSi2 Type of Structure: Synthesis, Crystal Structure and Magnetic Properties

Single crystals of CeAgAs2 have been obtained by chemical transport reactions starting from a pre‐reacted powder sample. The crystal structure was solved using X‐ray diffraction (space group Pmca, No. 57, a = 5.7586(4) Å, b = 5.7852(4) Å, c = 21.066(3) Å, Z = 8) and refined to a residual of R(F) = 0.029 for 46 refined parameters and 1020 reflections. The structure of CeAgAs2 represents a new distorted and ordered variant of the HfCuSi2 type. The characteristic feature of this structure are infinite cis‐trans chains of As atoms with As—As distances of 2.563(1) Å and 2.601(1) Å. CeAgAs2 is paramagnetic (μeff = 2.37 μB, θ = —10.5(2) K), with antiferromagnetic ordering at 5.5(2) K and exhibits a metamagnetic transition starting at 4.6 kOe and T = 1.8 K. CeAgAs2 — ein neuer Abkömmling des HfCuSi2‐Strukturtyps: Synthese, Kristallstruktur und magnetische Eigenschaften Einkristalle von CeAgAs2 konnten mittels chemischer Transportreaktionen ausgehend von einem vorreagierten Pulvermaterial dargestellt werden. Die Kristallstruktur wurde anhand von Röntgenbeugungsdaten gelöst (Raumgruppe Pmca, Nr. 57, a = 5.7586(4) Å, b = 5.7852(4) Å, c = 21.066(3) Å, Z = 8) und mit 46 Variablen bei 1020 Reflexen zu einem Residualwert von R(F) = 0.029 verfeinert. Die Atomanordnung von CeAgAs2 kann als eine verzerrte und geordnete Variante des HfCuSi2‐Typs aufgefasst werden. Die charakteristischen Strukturmerkmale sind cis‐trans‐Ketten von Arsenatomen mit Bindungsabständen von 2.563(1) Å und 2.601(1) Å. CeAgAs2 ist paramagnetisch (μeff = 2.37 μB, θ = —10.5(2) K) und ordnet antiferromagnetisch bei 5.5(2) K. Die Verbindung zeigt einen metamagnetischen Übergang bei 4.6 kOe und T = 1.8 K.