Copper Weberites: Crystal Structure and Magnetic Investigation of Na2CuGaF7 and Na2CuInF7

The crystal structures of two new copper weberites Na2CuGaF7 and Na2CuInF7 have been determined. Na2CuGaF7 has the monoclinic space group C2/c: a = 1232.5(5) pm, b = 731.8(1) pm, c = 1278.0(5) pm, β = 109.29(2)° and Z = 8. Na2CuInF7 crystallizes in the orthorhombic space group Pmnb: a = 731.8(1) pm, b = 1060.2(2) pm, c = 771.2(1) pm and Z = 4. The structures have been refined from 1175 reflections to R = 0.043 (wR = 0.035) for Na2CuGaF7, and from 1917 reflections to R = 0.034 (wR = 0.025) for Na2CuInF7. The structures consist of [CuF5]n3n− chains which are parallel the a‐axis in Na2CuInF7 and oriented in two alternating directions in Na2CuGaF7. Sodium atoms exhibit either seven‐fold or eight‐fold coordination. Although strong antiferromagnetic interactions are observed inside the chains, there is no evidence for three‐dimensional ordering. Kupferweberite: Kristallstruktur und magnetische Untersuchung von Na2CuGaF7 und Na2CuInF7 Die Kristallstruktur von zwei neuen Kupferweberiten Na2CuGaF7 und Na2CuInF7 wurde bestimmt. Na2CuGaF7: monokline Raumgruppe C2/c; a = 1232,5(5), b = 731,8(1), c = 1278,0(5) pm, β = 109,29(2)°, Z = 8. Na2CuInF7: orthorhombische Raumgruppe Pmnb; a = 731,8(1) pm, b = 1060,2(2) pm, c = 771,2(1) pm Z = 4. Die Strukturen wurden verfeinert mit 1175 Reflexen bis zu R = 0,043 (wR = 0,035) für Na2CuGaF7 und mit 1917 Reflexen bis zu R = 0,034 (wR = 0,025) für Na2CuInF7. Die Strukturen bestehen aus [CuF5]n3n−−Ketten, die im Na2CuInF7 parallel zur a‐Achse orientiert sind und in zwei alternierenden Richtungen im Na2CuGaF7. Die Natriumatome besitzen entweder siebenfache oder achtfache Koordination. Obwohl starke antiferromagnetische Wechselwirkungen innerhalb der Ketten beobachtet werden, gibt es keine Hinweise auf eine dreidimensionale Ordnung.