Cosmparative study of the ordering of B-S ite cations in Pb2ScTaO6 and Pb2ScNbO6 perovskites

A comparative study of as‐g rown Pb2ScTaO6 and Pb2ScNbO6 crystals obtained under similar conditions is made by X‐r ay and electron diffraction and by HREM at room temperature. From this study it can be concluded that: (i) the average distribution of atoms gives a cubic unit cell for both compounds though the study is conducted at a temperature close to Tc for PST, and lower than Tc for PSN; (ii) PST and PSN present the classical {111}‐type ordering and PST material has always a higher degree of ordering than PSN when they are prepared under similar conditions; (iii) small domains of {110}‐type ordering are observed in these two compounds leading to supplementary reflections, even by X‐r ay diffraction in the case of PSN. Une étude comparative des pérovskites Pb2ScTaO6 et Pb2ScNbO6 non recuites et obtenues dans des conditions semblables a été réalisée à température ambiante par diffraction de rayons X et d'électrons, ainsi que par MEHR. D'après cette étude nous pouvons déduire que: (i) La distribution atomique moyenne conduit à un réseau cristallin de maille cubique pour les deux composés, bien que l'étude soit réalisée à une température proche de Tc pour PST et inférieure à Tc pour PSN. (ii) PST et PSN présentent un ordre de type {111}, mais le degré d'ordre pour PST est toujours supérieur à celui de PSN (PST et PSN étant préparés dans les měmes conditions). (iii) De petits domaines d'ordre de type {110} apparaissent dans ces deux composés conduisant à des réflexions supplémentaires, observées měme par diffraction de rayons X dans le cas de PSN.