Study of metallic glasses rapidly quenched in magnetic field

The in‐plane magnetic anisotropy is measured for FeCrB amorphous alloys rapidly quenched in magnetic field by using FMR technique and BH curve measurements. The magnetic moment and the Curie temperature decrease but the anisotropy has a maximum with increasing Cr content. BH curve measurements show that the magnetic field applied during quenching results in an increase of the bulk in‐plane anisotropy. The FMR experimental results suggest that the random surface anisotropy due to surface irregularities is higher than the surface in‐plane anisotropy due to the effect of magnetic field in the quenching process. Mittels FMR‐Technik und BH‐Kurven‐Messungen wird die magnetische Anisotropie in der Ebene für amorphe FeCrB‐Legierungen untersucht, die im Magnetfeld schnell abgeschreckt werden. Das magnetische Moment und die Curietemperatur nehmen ab, jedoch zeigt die Anisotropie ein Maximum mit wachsendem Cr‐Gehalt. BH‐Kurvenmessungen zeigen, daß das während des Abschreckens angelegte Magnetfeld zu einem Anwachsen der Volumenanisotropie in der Ebene führt. Die experimentellen FMR‐Ergebnisse weisen darauf hin, daß die statistische Oberflächenanisotropie infolge von Oberflächenirregularitäten höher ist als die Oberflächenanisotropie in der Ebene infolge des Einflusses des Magnetfelds während des Abschreckungsprozesses.