Photoeletrochemical Properties of TiO2 Films Modified with Gold Nanoparticles

A nano‐Au modified TiO2 electrode was prepared via the oxidation of Ti sheet in flame and subsequent modification with gold nanoparticles. The results of SEM and TEM measurements show that the Au nanoparticles are well dispersed on TiO2 surface. A near 2‐fold enhancement in photocurrent was achieved upon the modification with Au nanoparticles. From the results of photocurrent and electrochemical impedance experiments it was found that the flatband potential of nano‐Au/TiO2 electrode negatively shifted about 100 mV in 0.5 mol/L Na2SO4 solutions compared with that of bare TiO2 electrode. The improvement of photoelectrochemical performance was explained by the inhibition for charge recombination of photo‐induced electrons and holes, and the promotion for interfacial charge‐transfer kinetics at nano‐Au/TiO2 composite film. Such nanometal‐semiconductor composite films have the potential application in improving the performance of photoelectrochemical solar cells.