The effects of polymerization mode and layer thickness on monomer released from bulk fill composite resins

Background: Residual monomers released from composite resins have cytotoxic, mutagenic, and estrogenic effects. Mode of polymerization and application thickness are important for monomer release. Aims: The aim of this study was to investigate the effects of different modes of a third-generation light-curing unit (LCU) and layer thickness on residual monomer released from two different bulk-fill composite resins. A total of 80 samples were prepared for each bulk-fill composite using a mold. Each bulk-fill composite was divided into four groups according to polymerization mode (standard and extra power) and layer thickness (2 and 4 mm). In addition, four groups were divided into four subgroups according to time periods (1 h, 24 h, 3 days, and 7 days). Methods and Material: The samples were polymerized with VALO LED device. The amount of residual monomer was measured with High-Performance Liquid Chromatography (HPLC). All statistical analyses were processed using SPSS Version 23.0. The normal distribution of data was confirmed using Kolmogorov-Smirnov Normal Distribution Test and Shapiro-Wilk Normal Distribution Test. When the distribution was normal, parametric tests, Student's t test and one-way ANOVA, were used. When the distribution was not normal, non-parametric tests, Mann-Whitney U test, and Kruskal-Wallis testwere used. Results: It was found that the standard mode of LCU produced lower amounts of TEGDMA, Bis-GMA, and UDMA in both composite materials. In addition, when the layer thickness increased, TEGDMA, Bis-GMA, and UDMA releases increased, too. Conclusions: This study revealed that the amount of residual monomers released from bulk-fill composites was affected by layer thickness and polymerization time.