Synthesis and microwave absorption properties of coralloid core-shell structure NiS/Ni3S4@PPy@MoS2 nanowires

[Display omitted] Herein, coralloid core-shell structure NiS/Ni3S4@PPy@MoS2 nanowires were elaborately designed and successfully synthesized through a three-step route to obtain exceptional microwave absorption (MA) properties. Ni nanowires were first fabricated, and then used as the substrate to be coated with a layer of PPy. Ni chalcogenides were obtained by using Ni nanowire as sacrificial templates while growing MoS2 nanorods by hydrothermal method. Both the one-dimensional (1D) core-shell structure and the coralloid surface generated by MoS2 nanorods were beneficial for the attenuation of microwaves. After investigating the electromagnetic properties of different loading content absorbers (30 wt.%, 40 wt.% and 50 wt.%), it is found that the 50 wt.% loading absorber has the optimal MA performance. The minimum reflection loss (RLmin) value can reach −51.29 dB at 10.1 GHz with a thickness of 2.29 mm, and the corresponding effective absorption bandwidth (EAB, RL