Synergistic Effects of Ladder and Cage Structured Phosphorus-Containing POSS with Tetrabutyl Titanate on Flame Retardancy of Vinyl Epoxy Resins

The cage and ladder structured phosphorus-containing polyhedral oligomeric silsesquioxanes (DOPO-POSS) have been synthesized through the hydrolytic condensation of 9,10-dihydro-9-oxa-10-phosphenanthrene-10-oxide (DOPO)-vinyl triethoxysilane (VTES). The unique ladder and cage-ladder structured components in DOPO-POSS endowed it with good solubility in vinyl epoxy resin (VE), and it was used with tetrabutyl titanate (TBT) to construct a phosphorus-silicon-titanium synergy system for the flame retardation of VE. Thermal stabilities, mechanical properties, and flame retardancy of the resultant VE composites were investigated by thermal gravimetric analysis (TGA), dynamic mechanical analysis (DMA), three-point bending tests, limiting oxygen index (LOI) measurement, and cone calorimetry. The experimental results showed that with the addition of only 4 wt% DOPO-POSS and 0.5 wt% TBT, the limiting oxygen index value (LOI) increased from 19.5 of pure VE to 24.2. With the addition of DOPO-POSS and TBT, the peak heat release rate (PHRR), total heat release (THR), smoke production rate (SPR), and total smoke production (TSP) were decreased significantly compared to VE-0. In addition, the VE composites showed improved thermal stabilities and mechanical properties comparable to that of the VE-0. The investigations on pyrolysis volatiles of cured VE further revealed that DOPO-POSS and TBT exerted flame retardant effects in gas phase. The results of char residue of the VE composites by SEM and XPS showed that TBT and DOPO-POSS can accelerate the char formation during the combustion, forming an interior char layer with the honeycomb cavity structure and dense exterior char layer, making the char strong with the formation of Si-O-Ti and Ti-O-P structures.