Creep behavior of ageing hardened Mg-10Gd-3Y alloy

Tensile creep behaviors of the ageing hardened Mg-10Gd-3Y alloy（referred to GW103）were investigated at temperatures up to 300℃.The extruded-T5 specimen exhibited high creep resistance,i.e.the low steady-state creep rate and long creep rupture time,while the better creep properties were observed in the cast-T6 one.The low steady-state creep rate of 1.71×10^- 9s^-1 is obtained at 200℃and 80 MPa for the extruded-T5 GW103 alloy.In addition,the microstructure development of GW103-T5 alloy was also examined after creep exposure at different temperatures.On the other hand,the stress exponent and activation energy were studied in the temperature range of 200-300℃for the extruded-T5 specimens,and the creep mechanism was also discussed.