Preparation of pure SbCl3 from lead anode slime bearing high antimony and low silver

TG1; A novel treatment process of lead anode slime bearing high antimony and low silver was developed by a potential-controlled chloridization leaching and continuous distillation. The experimental results show a high Sb3+concentration, 489.2 g/L, in the leaching solution for two-stage countercurrent leaching process, and the leaching rates of Sb, Cu, Bi more than 99% when the potential is controlled at 450 mV. When the leaching solution is distillated and concentrated at 120 ℃, almost all the silicon compound is evaporated into the concentration distillate and exists as amorphous hydrated silica. By the continuous distillation, high pure SbCl3 could be prepared, and AsCl3 is enriched in the distillate while metals Bi, Cu are enriched in the continuous distillation residue. As a result, the recovery rate of Sb is more than 95%.