Ni-BaTiO3 interface phenomenon of Co-fired PTCR by aqueous tape casting

The green sheets with Ni paste as inner electrodes were sintered at 1 320 ℃ for 1 h under a N2/H2 mixing gas at an oxygen partial pressure p（O2）=10-8-10-12 MPa, and then reoxided at 900-1 000 ℃ to form multilayer positive temperature coefficient of resistance（PTCR）. During the experiments, electronic characteristic effects of PTC with different thicknesses were contrasted. A certain extending of Ni diffusion is beneficial to the ohmic contact of multilayer PTCR but excessive diffusion is harmful to PTCR. The diffusion was studied by scanning electron microscopy（SEM） and energy-dispersive X-ray spectrometry（EDS）. Inter-diffusion of element takes place along the Ni-BaTiO3 interface, especially Ni diffusion to BaTiO3 dominated the process. Furthermore, the degree of Ni diffusion is very severe as ceramic layers are very thin.