Microstructure and mechanical properties of as-cast and heat treated Mg-15Gd-3Y alloy

The microstructure evolution and mechanical properties of Mg-15Gd-3Y alloy were investigated in the as-cast and heat treated conditions. The microstrucmre evolution from as-cast to cast-T4 states involved a-Mg solid solution＋Mg5（Gd,Y） phase→a-Mg supersaturated solid solution＋rare earths compound Mg3（Gdl.26,Y0.74）→a-Mg supersaturated solid solution＋rare earths compound Mg3（Gd0.Tas,Y1.255）. It showed that 480 ℃/4 h was the optimal solution treatment parameter. If the solution temperature was high or the holding time was long, such as 520 ℃/16 h, an overheating phenomenon would be induced, which had a detrimental effect on the mechanical properties. When ageing at 225 and 200℃, the alloy would exhibit a significant age-hardening response and great long-time-age-hardening potential, respectively. The best mechanical properties were obtained at the parameters of 480 ℃/4 h＋225 ℃/16 h, with the UTS of 257.0 MPa and elongation of 3.8%.