Modification of ZnS∶Mn Phosphors by Sb-Doped SnO2 Coating

TN3; The coating of ZnS∶Mn by Sb-doped SnO2 using an co-precipitation process was reported. ZnS∶Mn phosphor particles were prepared by solid reaction with ZnS and MnCl2·4H2O. Surface modification of the ZnS∶Mn powders was carried out by coating transparent conductive films of Sb-doped tin oxides which were formed by co-precipitation and heat treatment process. Tin tetrachloride and antimony trichloride were used as the precursor materials for the co-precipitation. The influences of coating molar ratio, Sb concentration in the coatings, annealing temperature and time on the resistivity of coated ZnS∶Mn phosphors were investigated. The optimum co-precipitation processing parameters and annealing conditions were determined. The phosphors were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), photoluminescence(PL) observation and conductance measurements. An improvement in phosphors conductivity was observed while the respective photoluminescence intensity is analogous to the as-prepared ZnS∶Mn phosphors.