Preparation of Poly-α-Olefin Microcapsule Particles Coated with Polyurethane as a Drag Reducer Based on Interface Polymerization

The molecular behavior of polyurethane(PU)coating materials during the surface adsorption of poly-α-olefin as a drag reducing polymer was explored by a molecular dynamics simulation.Three different PU capsule wall materials were synthesized using two reaction monomers,and a poly-α-olefin/PU drag reducer microcapsule was prepared based on interface polymerization.The structure,morphology,thermal stability,compressive strength,and drag reduction performance of the microcapsules were characterized and compared.The results showed that a non-bonding interaction induced the adsorption of the PU coating material,poly-α-olefin and PU then fused at the interface,and the PU coating material was embedded into the inner grooves of poly-α-olefin in the form of a local mosaic,thereby forming a stable core–shell structure.The morphological characterization indicated that PU and poly-α-olefin could form microcapsule structures.The thermal decomposition temperature of the microcapsule was dependent on the type of capsule wall material.The microcapsule structure had a slight effect on poly-α-olefin drag reduction.The system enabled poly-α-olefin to exist in powdered particles through microcapsulation,and had a good dispersion effect that facilitated storage and transport processes.The method effectively inhibited the accumulation and bonding of poly-α-olefin at room temperature.