Influence of Heating Rate and Calcining Temperature on Properties of 95 Polycrystalline Alumina Fiber

The swung gel fibers were hea, ted to 400 ℃ at 0. .5 ,1, 1.5,2,2.5,3and4 ℃ min^-1 of heating rate, respectivel, and soaked.for 1 h ; then heated to 600 ℃ at 3 ℃ min ^-1 of.heating rate amt soaked for 1 h at last calcined m 1 000, 1 100, 1 200, 1 300, and 1 400 ℃.for 1 h, respectively.

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	China's refractories 2012, Vol.21 (3), p.29-33
Hauptverfasser:	Xu, J, Fu, S, Liu, L, Jia, J, Gan, X
Format:	Artikel
Sprache:	eng
Schlagworte:	Aluminum oxide Fibers Fibres Forming Heating rate Refractories Roasting Tensile strength 凝胶纤维加热速度加热速率升温速率多晶氧化铝纤维小时属性煅烧温度
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The swung gel fibers were hea, ted to 400 ℃ at 0. .5 ,1, 1.5,2,2.5,3and4 ℃ min^-1 of heating rate, respectivel, and soaked.for 1 h ; then heated to 600 ℃ at 3 ℃ min ^-1 of.heating rate amt soaked for 1 h at last calcined m 1 000, 1 100, 1 200, 1 300, and 1 400 ℃.for 1 h, respectively.
ISSN:	1004-4493