Effect of oxygen precipitates in solar grade silicon on minority carrier lifetime and efficiency of solar cells
TG1; The effect of oxygen precipitates on minority carrier lifetime and performance of solar cell was studied by means of Fourier Transform Infrared Spectroscopy (FTIR), quasi-steady state photoconductance (QSSPCD), optical microscope, spectrumresponse and solar cell efficiency test. The minority ca...
Gespeichert in:
Veröffentlicht in: | 稀有金属(英文版) 2006, Vol.25 (z1), p.141-145 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | TG1; The effect of oxygen precipitates on minority carrier lifetime and performance of solar cell was studied by means of Fourier Transform Infrared Spectroscopy (FTIR), quasi-steady state photoconductance (QSSPCD), optical microscope, spectrumresponse and solar cell efficiency test. The minority carrier lifetime and performance of solar cell reduced depend on oxygen precipitates. A few of oxygen precipitates have formed after single-step annealing; and they do not impact the efficiency dramatically. Pre-annealing at 650 ℃ for 4 h enhances the oxygen precipitation when it is subjected to middle temperature annealing. The solar cells performance decayed sharply. Especially annealing at 950 ℃ for 3 h, the V os and I sc of cells decrease 12% and 25% respectively. Few oxygen precipitates have formed in silicon after high temperature annealing at about 1050 ℃ whether pre-annealing is used or not, and the performance of cells is notbe affected. |
---|---|
ISSN: | 1001-0521 |