Performance and mechanism study for low-temperature SCR of NO with propylene in excess oxygen over Pt/TiO2 catalyst

A 0.5 wt.% Pt/TiO2 catalyst was prepared and used for the low-temperature selective catalytic reduction （SCR） of NO with C3H6 in the presence of excess oxygen. The effects of Pt loading and 02 concentration on Pt/TiO2 catalytic performance for low-temperature SCR were investigated. It was found that optimal Pt loading was 0.5 wt.% and excess 02 favored low-temperature SCR of NOx. The mechanism of low-temperature SCR of NO with C3H6 was investigated with respect to the behavior of adsorbed species over Pt/TiO2 at 150~C using in situ DRIFTS. The results indicated that surface nitrosyl species （Pt~＋-NO and Ti3＋-NO） and pt2＋-CO are main reaction intermediates during the interactions of NO, C3H6 and 02. A simplified NO decomposition mechanism for the low-temperature SCR of NO with C3H6 was proposed.