Photoluminescence Properties of Two-dimensional Planar Layer and Three-dimensional Island Layer for ZnO Films Grown Using MOCVD

ZnO（002） films with different thicknesses ranging from 7 to 300 nm were grown on sapphire（006） substrates via metal-organic chemical vapor deposition （MOCVD）. The two-dimensional（2D） planar layer and the three-dimensional（3D） island layer were studied by using of X-ray diffraction（XRD） rocking curves and atomic force microscopy （AFM）. The room temperature photoluminescence （PL） spectra show a blue shift of the peak positions of the uhraviolet（UV） emission with increasing film thickness. The blue shift is remarkably high（393-380 nm） when an increase in film thickness（7-15 nm） is accompanied by the change of structure from a 2D planar layer to a 3D island layer. The PL spectra at 77 K also indicate that there are different transition mechanisms in the film thickness from a 2D planar layer to a 3D island layer near the 2D layer region.