Preparation and Characterization of PANI/PET Composite Conductive Fabric

Polyaniline /Polyester（ PANI /PET） composite conductive fabric is prepared through in-situ polymerization process using aniline as monomer and PET fabric as matrix,which is treated with alkali deweighting and low temperature plasma. The property of PANI /PET composite conductive fabric is studied and characterized,including scanning electron microscope（ SEM）, infrared spectroscopy, conductivity, wash fastness and mechanical properties. The results show that the optimal polymerization conditions： the molar ratio of ammonium persulfate and aniline is1∶ 1,the concentration of sulfuric acid is 1 mol /L and reaction time is 90 min. Under optimum conditions,the surface resistivity of PANI /PET composite conductive fabric is about 170 Ω. After washed 5 times, the surface resistivity of PANI /PET composite conductive fabric is stable at 1 450 Ω. The breaking strength and breaking elongation of PANI /PET composite conductive fabric decrease compared with PET fabric.