Microstructure evolution and mechanical properties of a large-sized ingot of Mg–9Gd–3Y–1.5Zn–0.5Zr(wt%) alloy after a lower-temperature homogenization treatment

In this paper,a large-sized ingot of Mg–9Gd–3Y–1.5Zn–0.5Zr(wt%) alloy with a diameter of 600 mm was successfully prepared by the semi-continuous casting method.The alloy was subsequently annealed at a relatively low temperature of 430°C for 12 h as a homogenization treatment.The microstructure and room-temperature mechanical properties of the alloy were investigated systematically.The results show that the as-cast alloy contained a mass of discontinuous lamellar-shaped 18 R long-period stacking ordered(LPSO) phases with a composition of Mg10 Zn Y and an α-Mg matrix,along with net-shaped Mg5(Y,Gd) eutectic compounds at the grain boundaries.Most of the eutectic compounds dissolved after the homogenization treatment.Moreover,the amount and dimensions of the lamellar-shaped LPSO phase obviously increased after the homogenization treatment.The structure of the phase transformed into 14H-type LPSO with composition Mg12Zn(Y,Gd).The mechanical properties of the heat-treated large-sized alloy ingot are uniform.The ultimate tensile strength(UTS) and tensile yield strength(TYS) of the alloy reached 207.2 MPa and 134.8 MPa,respectively,and the elongation was 3.4%.The high performances of the large-sized alloy ingot after the homogenization treatment is attributed to the strengthening of the α-Mg solid solution and to the plentiful LPSO phase distributed over the α-Mg matrix.