Reductive leaching of manganese from low-grade pyrolusite ore in sulfuric acid using pyrolysis-pretreated sawdust as a reductant

Manganese （Mn） leaching and recovery from low-grade pyrolusite ore were studied using sulfiaric acid （H2SO4） as a leachant and pyrolysis-pretreated sawdust as a reductant. The effects of the dosage of pyrolysis-pretreated sawdust to pyrolusite ore, the concentration of sulfuric acid, the liquid/solid ratio, the leaching temperature, and the leaching time on manganese and iron leaching efficiencies were inves- tigated. Analysis of manganese and iron leaching efficiencies revealed that a high manganese leaching efficiency was achieved with low iron extraction. The optimal leaching efficiency was determined to be 20wt% pyrolysis-pretreated sawdust and 3.0 mol/L H2SO4 using a liq- uid/solid ratio of 6.0 mL/g for 90min at 90℃. Other low-grade pyrolusite ores were tested, and the results showed that they responded well with manganese leaching efficiencies greater than 98%.