Understanding the salinity effect on cationic polymers in inducing flocculation of the microalga Neochloris oleoabundans

•The mechanism of cationic polymeric flocculation at elevated salinities has been revealed.•Polymeric charge is a key parameter influencing flocculation.•Polymeric coiling is not affecting flocculation in marine conditions. A mechanistic study was performed to evaluate the effect of salinity on cationic polymeric flocculants, that are used for the harvesting of microalgae. The polyacrylamide Synthofloc 5080H and the polysaccharide Chitosan were employed for the flocculation of Neochloris oleoabundans. In seawater conditions, a maximum biomass recovery of 66% was obtained with a dosage of 90mg/L Chitosan. This recovery was approximately 25% lower compared to Synthofloc 5080H reaching recoveries greater than 90% with dosages of 30mg/L. Although different recoveries were obtained with both flocculants, the polymers exhibit a similar apparent polymer length, as was evaluated from viscosity measurements. While both flocculants exhibit similar polymer lengths in increasing salinity, the zeta potential differs. This indicates that polymeric charge dominates flocculation. With increased salinity, the effectivity of cationic polymeric flocculants decreases due to a reduction in cationic charge. This mechanism was confirmed through a SEM analysis and additional experiments using flocculants with various charge densities.