N-induced antibacterial capability of ZrO2-SiO2 glass ceramics by ion implantation

Periodontal disease caused by bacterial accumulation is a critical issue affecting the longevity of related materials and implants. Enhancing the antibacterial properties of glass ceramics remains a significant challenge. Due to their excellent mechanical properties, ZrO2-SiO2 glass ceramics have shown great potential in dental restoration. Here, to endow ZrO2-SiO2 glass ceramics with antibacterial properties, nitrogen ion implantation was performed to modify their surfaces. The effects of nitrogen fluence on the microstructural, mechanical and antibacterial properties were investigated. The results showed that phase transformation from tetragonal to monoclinic phase occurred after ion implantation. Surface hardening was observed in the sample under the low fluence ion implantation. Partial amorphization and blistering were observed at the highest fluence of 6.0 1017 ions/cm2. XPS analysis revealed that the implanted nitrogen ions mainly form O-Zr-N, N-Si-O and Si-N bonds. Staphylococcus aureus testing showed that the antibacterial properties of ZrO2-SiO2 glass ceramics can be enhanced after implantation, which may be attributed to the formation of reactive nitrogen species. The results show that nitrogen implantation can enhance the antibacterial properties of ZrO2-SiO2 glass ceramics without compromising their mechanical properties.