Effect of low-temperature degradation on the mechanical and microstructural properties of tooth-colored 3Y-TZP ceramics

The aim of the present study was to evaluate the effects of low-temperature degradation (LTD) induced by autoclaving on the mechanical and microstructural properties of tooth-colored 3mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP). In total, 162 disc-shaped 3Y-TZP specimens were prepared. Two-thirds of the specimens were shaded by either the infiltration or powder mixing methods while the remaining specimens were used without coloring. The specimens were autoclaved at 134°C for 0, 10, and 100h to induce LTD (n=18 for each group). Chemical compositions were analyzed with X-ray fluorescence spectroscopy. Biaxial flexural strength was measured using a piston-on-three-ball test. The surface fraction and penetration depth of the monoclinic phase were examined using X-ray diffraction and scanning electron microscopy, respectively. The tooth-colored 3Y-TZP specimens contained Fe2O3 and Er2O3 (infiltration technique), and Fe2O3 (powder mixing method) at concentrations of