Decreased bacterial colonization of additively manufactured Ti6Al4V metallic scaffolds with immobilized silver and calcium phosphate nanoparticles

The design of an ideal bone graft substitute has been a long-standing effort, and a number of strategies have been developed to improve bone regeneration. Electron beam melting (EBM) is an additive manufacturing method allowing for the production of porous implants with highly defined external dimensions and internal architectures. The increasing surface area of the implant may also increase the abilities of pathogenic microorganisms to adhere to the surfaces and form a biofilm, which may result in serious complications. The aim of this study was to explore the modifications of Ti6Al4V alloy scaffolds to reduce the abilities of bacteria to attach to the EBM-manufactured implant surface. The layers composed of silver (Ag), calcium phosphate (CaP) nanoparticles (NPs) and combinations of both were formed on the EBM-fabricated metallic scaffolds by electrophoretic deposition in order to provide them with antimicrobial properties. The assay of bacterial colonization on the surface was performed with the exposure of scaffold surfaces to Staphylococcus aureus cells for up to 17 h. Principal component analysis (PCA) was used to assess the relationships between different surface features of the studied samples and bacterial adhesion. The results indicate that by modifying the implant surface with appropriate nanostructures that change the hydrophobicity and the surface roughness at the nano scale, physical cues are provided that disrupt bacterial adhesion. Our results clearly show that AgNPs at a concentration of approximately 0.02 mg/сm2 that were deposited together with CaPNPs covered by positively charge polyethylenimine (PEI) on the surface of EBM-sintered Ti6Al4V scaffolds hindered bacterial growth, as the total number of attached cells (NAC) of S. aureus remained at the same level during the 17h of exposure, which indicates bacteriostatic activity. [Display omitted] •Different modifications of 3D-printed Ti6Al4V alloy scaffolds were investigated.•Antibacterial activity of different modifications of Ti6Al4V scaffolds was studied.•The layers of silver, and calcium phosphate nanoparticles were used.•The change of wetting behavior and surface roughness disrupted bacterial adhesion.