Single lamellar mechanics of the human lumbar anulus fibrosus

The mechanical behavior of the entire anulus fibrosus is determined essentially by the tensile properties of its lamellae, their fiber orientations, and the regional variation of these quantities. Corresponding data are rare in the literature. The paper deals with an in vitro study of single lamellar anulus lamellae and aims to determine (i) their tensile response and regional variation, and (ii) the orientation of lamellar collagen fibers and their regional variation. Fresh human body-disc-body units (L1-L2, n=11) from cadavers were cut midsagittally producing two hemidisc units. One hemidisc was used for the preparation of single lamellar anulus specimens for tensile testing, while the other one was used for the investigation of the lamellar fiber orientation. Single lamellar anulus specimens with adjacent bone fragments were isolated from four anatomical regions: superficial and deep lamellae (3.9+/-0.21 mm, mean +/- SD, apart from the outer boundary surface of the anulus fibrosus) at ventro-lateral and dorsal positions. The specimens underwent cyclic uniaxial tensile tests at three different strain rates in 0.15 mol/l NaCl solution at 37 degrees C, whereby the lamellar fiber direction was aligned with the load axis. For the characterization of the tensile behavior three moduli were calculated: E(low) (0-0.1 MPa), E(medium) (0.1-0.5 MPa) and E(high) (0.5-1 MPa). Additionally, specimens were tested with the load axis transverse to the fiber direction. From the second hemidisc fiber angles with respect to the horizontal plane were determined photogrammetrically from images taken at six circumferential positions from ventral to dorsal and at three depth levels. Tensile moduli along the fiber direction were in the range of 28-78 MPa (regional mean values). Superficial lamellae have larger E(medium) (p=0.017) and E(high) (p=0.012) than internal lamellae, and the mean value of superficial lamellae is about three times higher than that of deep lamellae. Tensile moduli of ventro-lateral lamellae do not differ significantly from the tensile moduli of dorsal lamellae, and E(low) is generally indifferent with respect to the anatomical region. Tensile moduli transverse to the fiber direction were about two orders of magnitude smaller (0.22+/-0.2 MPa, mean +/- SD, n=5). Tensile properties are not correlated significantly with donor age. Only small viscoelastic effects were observed. The regional variation of lamellar fiber angle phi is described appropriately by a r