Effect of solution heat treatments on superalloys Part 1 - alloy 718

The hot ductility as measured by Gleeble testing of Alloy 718 at four different solution heat treatments (954°C/15 h, 954°C/1 h, 982°C/1 h and 1050°C/3 h+954°C/1 h) has been investigated. It is concluded that constitutional liquation of NbC assisted by δ phase takes place and deteriorates the ductility. Parameters established by analysing the ductility dependence on temperature indicate a reduced weldability of the material in the coarse grain size state (ASTM 3) while indicating an increased weldability when containing a large amount of δ phase due to a grain boundary pinning effect. The accumulation of trace elements during grain growth at the highest temperature is believed to be the cause for the observed reduced on-cooling ductility.