Laser Welding and Additive Manufacturing of Duplex Stainless Steels: Properties and Microstructure Characterization

Duplex stainless steels (DSS), with a ferritic-austenitic microstructure, are used ina wide range of applications thanks to their high corrosion resistance and excellent mechanical properties. However, efficient and successful production and joining of DSS require precise control of processes and an in-depth understanding o frelations between composition, processing thermal cycles, resulting microstructures and properties. In this study laser welding, laser reheating, and laser additive manufacturing using Laser Metal Deposition with Wire (LMDw) ofDSS and resulting weld and component microstructures and properties are explored. In the first part a lean FDX 27 duplex stainless steel, showing the transformation induced plasticity (TRIP) effect, was autogenously laser welded and laser reheated using pure argon or pure nitrogen as shielding gas. The weld metal austenite fraction was 22% for argon-shielding and 39% for nitrogen-shielding in as-welded conditions. Less nitrides were found with nitrogen-shielding compared to argonshielding. Laser reheating did not significantly affect nitride content or austenite fraction for argon-shielding. However, laser reheating of the nitrogen shieldedweld removed nitrides and increased the austenite fraction to 57% illustrating the effectiveness of this approach. Phase fraction analysis is important for DSS since the balance between ferrite and austenite affects properties. For TRIP steels the possibility of austenite tomartensite transformation during sample preparation also has to be considered. Phases in the laser welded and reheated FDX 27 DSS were identified and quantified using light optical microscopy (LOM) and electron backscatter diffraction (EBSD) analysis. An optimized Beraha color etching procedure was developed for identification of martensite by LOM. A novel step-by-step EBSD methodology was also introduced, which successfully identified and quantified martensite as well as ferrite and austenite. It was found that mechanical polishing produced up to 26% strain-induced martensite, while no martensite was observed after electrolytic polishing.In the second part a systematic four-stage methodology was applied to develop procedures for additive manufacturing of standard 22% Cr duplex stainless steel components using LMDw combined with the hot wire technology. In the four stages, single-bead passes, a single-bead wall, a block, and finally a cylinder with an inner diameter of 160 mm, thickness of 30 mm, and height