Influence of microstructure on the erosion behaviour of suspension plasma sprayed thermal barrier coatings

Thermal barrier coatings (TBCs) are applied on the surface of hot parts of gas turbine engines to increase the turbine efficiency by providing thermal insulation and to protect the engine parts from the harsh environment. Typical degradation of TBCs can be attributed to bond coat oxidation, thermal stress etc. In addition to this, erosion can also lead to partial or complete removal of the TBCs especially when the engine operates under erosive environment such as flying over desert area, near active volcanic or offshore ocean environment. Suspension Plasma Spraying (SPS) is a promising technique for TBC applications by virtue of its ability to produce a strain-tolerant porous-columnar microstructure that combines the benefits of both electron beam physical vapor deposited (EB-PVD) as well as atmospheric plasma sprayed (APS) coatings. This work investigates the influence of various coating microstructures produced by SPS on their erosion behavior. Six different coatings with varied microstructures produced using different suspensions with distinct characteristics were studied and their erosion resistance was compared. Results showed significant influence of SPS TBCs microstructures on the erosion resistance. Furthermore, the erosion resistance of SPS TBCs showed a close correlation between fracture toughness and the erosion rate, higher fracture toughness favours superior erosion resistance. •.•8YSZ was used to prepare six distinct suspension by varying solvent type, solid load content and particle size distribution.•Microstructural influence on erosion performance was investigated for SPS 8YSZ TBC.•The mechanical properties and porosity measurement were investigated.•Erosion model was proposed for different type of microstructure i.e. columnar and vertically cracked sprayed with SPS.