Excellent energy storage properties, domain mechanism, and temperature stability of lead-free BaTiO3-Bi(Mg1/2Sn1/2)O3 bulk ferroelectrics
Pulsed power systems require high-performance capacitors with high energy storage density. In this work, (1 − x)BaTiO3-xBi(Mg1/2Sn1/2)O3 ferroelectric ceramics were synthesized in a solid-state solution. The sample of x = 0.12 (0.88BT-0.12BMS) has excellent energy storage density, wide temperature,...
Gespeichert in:
Veröffentlicht in: | Applied physics letters 2023-04, Vol.122 (17) |
---|---|
Hauptverfasser: | , , , , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Pulsed power systems require high-performance capacitors with high energy storage density. In this work, (1 − x)BaTiO3-xBi(Mg1/2Sn1/2)O3 ferroelectric ceramics were synthesized in a solid-state solution. The sample of x = 0.12 (0.88BT-0.12BMS) has excellent energy storage density, wide temperature, and wide frequency stability. The excellent energy density of 4.87 J/cm3 at 315 kV/cm and the energy efficiency of 72% at room temperature for 0.88BT-0.12BMS ceramics were achieved. Furthermore, the 0.88BT-0.12BMS ceramics demonstrated well temperature stabilities in the range of 20–100 °C and very good frequency stability in the range of 1–100 Hz. Through pulsed charging–discharging testing, the current density is calculated as 314.01 A/cm2, and the power density is 21.98 MW/cm3. Moreover, the oxygen vacancies' defects and ferroelectric domain mechanism for enhanced breakdown strength as well as high energy density were discussed. These findings broaden the horizon for lead-free dielectrics and show promising applications for pulse power capacitors. |
---|---|
ISSN: | 0003-6951 1077-3118 |
DOI: | 10.1063/5.0137616 |