Self-induced ferroelectric 2-nm-thick Ge-doped HfO2 thin film applied to Ge nanowire ferroelectric gate-all-around field-effect transistor

This paper reports a self-induced ferroelectric 2-nm-thick Ge-doped HfO2 (Ge:HfO2) thin film. Ge thermal desorption, incorporation into HfO2, and further Ge:HfO2 crystallization were all performed through rapid thermal annealing simultaneously. The ferroelectric property of a 2-nm-thick Ge:HfO2/2-nm...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Applied physics letters 2020-12, Vol.117 (26)
Hauptverfasser: Lin, Yi-Wen, Sun, Chong-Jhe, Chang, Hao-Hsiang, Huang, Yu-Hsien, Yu, Tung-Yuan, Wu, Yung-Chun, Hou, Fu-Ju
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:This paper reports a self-induced ferroelectric 2-nm-thick Ge-doped HfO2 (Ge:HfO2) thin film. Ge thermal desorption, incorporation into HfO2, and further Ge:HfO2 crystallization were all performed through rapid thermal annealing simultaneously. The ferroelectric property of a 2-nm-thick Ge:HfO2/2-nm-thick Al2O3 dielectric stack was confirmed using the polarization-electric field measurement. X-ray photoelectron spectroscopy was used to confirm that Ge bonded to HfO2 as Hf-germanates. Piezoresponse force microscopy was used to demonstrate the piezoelectric property of Ge:HfO2/Al2O3. Furthermore, a dielectric stack of Ge:HfO2/Al2O3 was applied as a gate insulator in a Ge nanowire gate-all-around ferroelectric field-effect transistor (Ge NW Fe-GAAFET). The device exhibited a minimum steep-sub-threshold slope of 47 mV/dec, a high ION/IOFF ratio of >106, and low gate leakage current; moreover, it was free of a drain-induced barrier lowering effect. The proposed self-induced ferroelectric Ge:HfO2 Ge NW Fe-GAAFET is feasible for future ultra-low power integrated circuit applications.
ISSN:0003-6951
1077-3118
DOI:10.1063/5.0029628