Dynamic resistance measurement in a YBCO wire under perpendicular magnetic field at various operating temperatures

Dynamic resistance plays an important role in certain high-Tc superconducting (HTS) applications where an HTS coated conductor carries a DC current exposed to an AC magnetic field. Here, we report measurements of the dynamic resistance in a 4 mm-wide YBCO coated conductor under a perpendicular AC magnetic field at 77 K, 70 K, and 65 K. Dynamic resistance was measured at three different frequencies for the reduced current, i (It/Ic0), ranging from 0.04 to 0.9, where It is the DC current level and Ic0 is the self-field critical current of the conductor at each temperature. At all three temperatures, the threshold magnetic field (Bth) values increase with reducing DC current. These results show that, for a given set of applied conditions, dynamic resistance decreases with decreasing operating temperature, which we attribute to the temperature dependent increase in the critical current of the wire. We show that measured Bth values at all three temperatures agree well with the analytical values from nonlinear Mikitik and Brandt equation for i ≤ 0.2 and with a simple linear expression that assumes a current-independent penetration field for i > 0.2. We further show the measured Bth curves at different temperatures normalized by critical current density collapse into one common curve. The above result implies that dynamic resistance in coated conductors at different temperatures under perpendicular AC magnetic fields can be scaled simply using measured Ic0 values at those temperatures and analytical equations.