Increasing the resistance of a NiCrBSi coating to heat wear by means of combined laser heat treatment

Testing of NiCrBSi coatings formed by gas-powder laser cladding and combined laser heat treatment, including laser cladding and high-temperature annealing, were conducted under conditions of sliding friction on the Kh12M steel according to the pin-on-disk scheme. The combined processing resulting in the formation of large carbides and chromium borides in the coatings is shown to increase their wear resistance by a factor of 1.8 at sliding velocities of 6.1 and 9.3 m/s, when there is significant frictional heating of the friction surfaces.