Dielectric and magnetic studies of Cr+3 doped nickel ferrite by combustion method

Cr+3 doped nickel ferrite nanoparticles having the basic composition NiCrxFe2-xO4 (x=0, 0.1, 0.15, 0.2, 1) were prepared using auto combustion method. Structural, dielectric, a.c conductivity and magnetic properties of these samples, which are sintered at 800°C were studied. The structures of the synthesized samples were probed by X-ray diffraction (XRD) studies. The peaks observed in the XRD spectrum indicated single phase spinel cubic structure for the synthesized samples. Surface morphology of the samples has been investigated using Field Emission Scanning Electron Microscope (FESEM). The dielectric constant (ε′) and dielectric loss factor (ε″) of nanocrystalline nickel ferrites were investigated as a function of frequency and Cr+3 concentration at room temperature over the frequency range 100 Hz to 1 MHz using Hioki make LCR Hi-Tester 3250. The dependence of ε′ and ε″ with the frequency of the alternating applied electric field is in accordance with the Maxwell-Wagner type interfacial polarization, which is in agreement with the Koop’s theory. The electrical conductivity (σac) deduced from the measured dielectric data has been thoroughly analyzed and found that the conduction mechanism in NiCrxFe2-xO4 nanoferrites are in conformity with the electron hopping model. The magnetic properties of Cr+3 doped nano-nickel ferrite were analyzed using a Vibrating Sample Magnetometer (VSM). It is observed that the values of saturation magnetization decreases along with the increase in chromium content.