Preparation and application of nanocrystalline cellulose derived from sugarcane waste as filler modified alkanolamide on crosslink of natural rubber latex film

Sugarcane waste is abundant sources of cellulose and it has potential to reutilize. Cellulose from sugarcane waste can be derived into nanocystalline cellulose (NCC) from crystalline region. The NCC as a filler has capability to reinforce natural rubber latex product. The crosslink in vulcanized natural rubber latex film influences several properties of product. In this work, we extracted NCC from sugarcane waste then added into natural rubber latex as filler modified alkanolamide (ALK) and also studied the crosslink of natural rubber latex films. NCC were produced from sugarcane waste by hydrolysis process with sulfuric acid 45%. The obtained NCC was characterized by using x-ray diffraction (XRD), transmission electron microscopy (TEM), and fourier transform infra red (FTIR). NCC was modified by alkanolamide and dispersed in water with filler concentration of 10%. Then the dispersion were added into latex system followed by pre-vulcanization at 70 °C. The films were prepared by coagulant dipping method and dried at 100 °C and 120 °C for 20 minutes. Characterization of NCC from sugarcane waste by using FTIR was done, it clearly showed the functional groups of cellulose. TEM showed the obtained NCC were rod-shaped with about 40-160 nm in diameter and several hundred nm in length, and XRD showed that the degree of crystalinity of NCC from sugarcane waste is 92.33%. The crosslink of natural rubber films were studied by measure the crosslink density for different filler loading by using swelling measurement with toluene solution. The result show that the crosslink density increased in line with amount of filler which added into the system, and also the crosslink density that obtained from vulcanization at 120 °C were higher than 100 °C.