Structural, ferroelectric, dielectric, and magnetic propertiesof BiFeO 3 / Bi 3.15 Nd 0.85 Ti 3 O 12 multilayer films derived by chemicalsolution deposition
BiFeO 3 / Bi 3.15 Nd 0.85 Ti 3 O 12 (BFO/BNdT) multilayer films have been grown on Pt-coated silicon substrate by chemical solution deposition. Using Bi 3.15 Nd 0.85 Ti 3 O 12 as an inducing layer, ferroelectric properties of BiFeO 3 were enhanced significantly. The 2 P r and coercive electric field...
Gespeichert in:
Veröffentlicht in: | Journal of applied physics 2009-04, Vol.105 (8), p.084109-084109-5 |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | BiFeO
3
/
Bi
3.15
Nd
0.85
Ti
3
O
12
(BFO/BNdT) multilayer films have been grown on Pt-coated silicon substrate by chemical solution deposition. Using
Bi
3.15
Nd
0.85
Ti
3
O
12
as an inducing layer, ferroelectric properties of
BiFeO
3
were enhanced significantly. The
2
P
r
and coercive electric field of the Pt/BFO/BNdT/Pt capacitor were about
22.1
μ
C
/
cm
2
and 50 kV/cm, respectively. The dielectric constant and the dissipation factor of the multilayer were 373 and 0.05 measured at
10
5
Hz
, respectively. The multilayer capacitors not only exhibited excellent fatigue resistance without polarization reduction after
10
10
switching cycles but also showed lower leakage current density (around the order of
10
−
9
-
10
−
7
A
/
cm
2
) and negligible data loss due to imprint. The magnetic hysteresis indicated that the multiplayer was antiferromagnetic and the saturated magnetization was about
2.47
emu
/
cm
3
. |
---|---|
ISSN: | 0021-8979 1089-7550 |
DOI: | 10.1063/1.3110074 |