Fracture resistance and failure pattern of teeth submitted to internal bleaching with 37% carbamide peroxide, with application of different restorative procedures
This study investigated the compressive fracture strength and failure pattern in premolars submitted to endodontic treatment and internal bleaching with 37% carbamide peroxide for 21 days, with application of different restorative procedures. Six groups were employed (n = 10): 1) non-bleached teeth...
Gespeichert in:
Veröffentlicht in: | Journal of applied oral science 2006-08, Vol.14 (4), p.247-252 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | This study investigated the compressive fracture strength and failure pattern in premolars submitted to endodontic treatment and internal bleaching with 37% carbamide peroxide for 21 days, with application of different restorative procedures.
Six groups were employed (n = 10): 1) non-bleached teeth and pulp chamber sealed with IRM; 2) bleached teeth and pulp chamber sealed with IRM; 3) bleached teeth and pulp chamber filled with light cured composite resin; 4) bleached teeth, root canals prepared at 10mm, filling of the root canal and pulp chamber with IRM; 5) bleached teeth, root canals prepared at 10mm, luting of prefabricated metallic post with zinc phosphate and pulp chamber sealed with composite resin; 6) bleached teeth, root canals prepared at 10mm, luting of glass fiber post with resin cement and pulp chamber sealed with composite resin. After 24-hour storage in distilled water, the specimens were submitted to compressive fracture strength testing in a universal testing machine.
The following values were found: Group 1 - 56.23kgf; Group 2 - 48.96kgf; Group 3 - 53.99kgf; Group 4 - 45.72kgf; Group 5 - 54.22kgf; Group 6 - 60.12kgf. The analysis of variance did not reveal statistically significant difference between groups (p |
---|---|