Comparative of flexural strength, hardness, and fluoride release of two bioactive restorative materials with RMGI and composite resin

Aim: This study was fulfilled to evaluate the flexural strength, micro-hardness, and release of two fluoride ions of bioactive restorative materials (Cention N and Activa Bioactive), a resin modified glass ionomer (Fuji II LC), and a resin composite (Filtek z250). Methods: Forty samples from four restorative materials (Activa Bioactive, Fuji II LC, Cention N, and Filtek Z250) were provided according to the current standards of ISO 4049/2000 guide lines. Subsequently, the samples were stored for 24 hours and 6 months in artificial saliva, and successively, flexural strength and micro-hardness of the samples were measured. For each studied groups the pH was decreased from 6.8 to 4 in storage solution. The rate of changes in fluoride ion release was measured after three different storage periods of 24 hours, 48 hours, and 6 months in distilled water, according to the previous studies’ method. Two-way ANOVA, One-way ANOVA, Tukey HSD Pair wise comparisons, and independent t-tests were used to analyze data (α= 0.05). Results: The highest flexural strength and surface micro-hardness after 24 hours and also after 6 month were observed for Cention N(p