Characterization of damage modes in impacted thermoset and thermoplastic composites

Composite materials remain extremely vulnerable to out-of-plane impact loads, which may lead to severe losses in strength and stiffness. Impact induced damage is often a complex mixture of transverse cracks, delaminations and fiber failures. An experimental investigation was undertaken to quantify damage tolerance and resistance in composite materials impacted using the drop-weight method. Tests were conducted on laminates of several different carbon-fiber composite systems such as epoxies, modified epoxies, and amorphous and semicrystalline thermoplastics. In this paper, impacted composite specimens have been examined using destructive and nondestructive techniques to establish the characteristic damage states. Specifically, optical microscopy, ultrasonic and scanning electron microscopy techniques have been used to identify impact induced damage mechanisms. Damage propagation during post impact compression was also studied.