A negative photoconductivity photodetector based on two-dimensional NbCl

Negative photoconductivity (NPC)-based photodetectors offer a new direction for energy-efficient photodetection technologies, featuring low energy consumption and high responsivity. Two-dimensional (2D) materials are particularly promising for implementing NPC due to their large surface area, abundant surface states, and tunable bandgap properties. In this context, 2D Nb 3 Cl 8 , with its unique kagome lattice structure and broad absorption spectrum, has attracted considerable interest. Notably, metal halides such as Nb 3 Cl 8 demonstrate significant potential as NPC materials due to their low anionic and cationic bonding strength, which allows for the formation of vacancy defects with high probability. However, the NPC characteristics of Nb 3 Cl 8 have not been thoroughly investigated. In this study, we fabricated field-effect transistors (FETs) using Nb 3 Cl 8 single crystals synthesized via chemical vapor transport (CVT). These devices exhibited an electron mobility of 4.24 × 10 −3 cm 2 V −1 s −1 and a high I on / I off ratio of 1.42 × 10 4 . Notably, Nb 3 Cl 8 -based photodetectors demonstrated consistent NPC behavior across a wide wavelength range of 400-1050 nm, with a high responsivity of 156.82 mA W −1 at 400 nm. We propose that the trapping effect due to defect levels within the bandgap is the primary cause of this NPC phenomenon. The present findings reveal the unique photodetector properties of Nb 3 Cl 8 and highlight its promise in energy-efficient photodetectors and various optoelectronic applications. We developed a Nb 3 Cl 8 -based photodetector with negative photoconductivity from 400 to 1050 nm, featuring high electron mobility, a strong I on /I off ratio, and high responsivity, making it ideal for energy-efficient optoelectronic applications.