A strongly coupled 3D SnS@TiCT heterojunction with vacancies for high-efficiency sodium storage
Ti 3 C 2 T x , as some of the typical MXenes, exhibit great potential for application in rechargeable batteries due to its high conductivity, low ionic diffusion resistance, adjustable layer spacing, and surface modifiability. However, several challenges hinder its practical value, including severe...
Gespeichert in:
Veröffentlicht in: | New journal of chemistry 2024-01, Vol.48 (4), p.151-1517 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Ti
3
C
2
T
x
, as some of the typical MXenes, exhibit great potential for application in rechargeable batteries due to its high conductivity, low ionic diffusion resistance, adjustable layer spacing, and surface modifiability. However, several challenges hinder its practical value, including severe self-stacking, low capacity, and unsatisfactory durability, particularly when accommodating large sodium ions. To address these issues, we have designed a SnS
2
@Ti
3
C
2
T
x
sandwich structure with S vacancies through heterojunction engineering. Anchoring SnS
2
to Ti
3
C
2
T
x
via
S-Ti-C bonds, this interlocking cooperative heterostructure not only mitigates Ti
3
C
2
T
x
self-stacking but also exposes a significant number of active sites on the surface. Consequently, it improves the intercalation pseudocapacitance ratio, resolves the reaction kinetic hysteresis caused by the challenging removal of sodium ions, and prevents structural collapse resulting from the volume effect in SnS
2
. Moreover, the S vacancies effectively enhance the adsorption capacity of Na
+
, providing additional active sites for their adsorption. Density functional theory calculations demonstrate increased adsorption energy and reduced diffusion energy of sodium ions, thereby improving the sodium storage performance of the materials. The SnS
2
@Ti
3
C
2
T
x
heterojunction exhibits an impressive reversible capacity of 225 mA h g
−1
at 100 mA g
−1
, with 82% capacity retention after 1000 cycles. Furthermore, even at 500 mA g
−1
, a capacity of 122 mA h g
−1
can still be achieved after 1000 cycles. Consequently, this research offers novel insights for future exploration in the development of anode materials for ion batteries.
We have developed a SnS
2
@Ti
3
C
2
T
x
sandwich structure through heterojunction engineering. By anchoring SnS
2
to Ti
3
C
2
T
x
, this interlocking cooperative heterostructure effectively mitigates Ti
3
C
2
T
x
self-stacking and exposes numerous active sites on the surface. |
---|---|