Steps towards highly-efficient water splitting and oxygen reduction using nanostructured β-Ni(OH)

β-Ni(OH) 2 nanoplatelets are prepared by a hydrothermal procedure and characterized by scanning and transmission electron microscopy, X-ray diffraction analysis, Raman spectroscopy, and X-ray photoelectron spectroscopy. The material is demonstrated to be an efficient electrocatalyst for oxygen reduction, oxygen evolution, and hydrogen evolution reactions in alkaline media. β-Ni(OH) 2 shows an overpotential of 498 mV to reach 10 mA cm −2 towards oxygen evolution, with a Tafel slope of 149 mV dec −1 (decreasing to 99 mV dec −1 at 75 °C), along with superior stability as evidenced by chronoamperometric measurements. Similarly, a low overpotential of −333 mV to reach 10 mA cm −2 (decreasing to only −65 mV at 75 °C) toward hydrogen evolution with a Tafel slope of −230 mV dec −1 is observed. Finally, β-Ni(OH) 2 exhibits a noteworthy performance for the ORR, as evidenced by a low Tafel slope of −78 mV dec −1 and a number of exchanged electrons of 4.01 (indicating direct 4e − -oxygen reduction), whereas there are only a few previous reports on modest ORR activity of pure Ni(OH) 2 . β-Ni(OH) 2 nanoplatelets produced via a hydrothermal method exhibit good performance as trifunctional electrocatalysts for the ORR, OER, and HER in alkaline media along with excellent stability under cathodic/anodic polarisation conditions.