Mechanochemical synthesis of an efficient nanocrystalline BaFBr:Eu2+ X-ray storage phosphor

A straightforward and direct preparation route for nanocrystalline BaFBr:Eu 2+ by ball-milling is reported. We demonstrate that the as-prepared nanocrystalline powder becomes an efficient photostimulable X-ray storage phosphor upon annealing at temperatures in the range of 400 to 900 °C. The depende...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Hauptverfasser: Wang, Xianglei, Riesen, Hans
Format: Artikel
Sprache:eng ; jpn
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:A straightforward and direct preparation route for nanocrystalline BaFBr:Eu 2+ by ball-milling is reported. We demonstrate that the as-prepared nanocrystalline powder becomes an efficient photostimulable X-ray storage phosphor upon annealing at temperatures in the range of 400 to 900 °C. The dependence of crystallite size, photoluminescence and storage phosphor properties on annealing temperature and annealing time was investigated and the optimal conditions were determined. After annealing at 900 °C for 1 h, the average crystallite size was found to be ∼200 nm. In comparison with the typical ∼5 μm particles for conventional phosphors, the shape and size distribution of the crystallites may allow higher packing densities, resulting in higher sensitivities, and resolution in computed radiography. The photostimulable storage properties compare favorably with results obtained for a commercial BaFBr(I):Eu 2+ imaging plate. We report on a facile mechanochemical preparation route to directly synthesise a highly efficient nanocrystalline BaFBr:Eu 2+ X-ray storage phosphor and its photostimulable luminescence efficiency.
ISSN:2046-2069
DOI:10.1039/c5ra16107j