Ab initio studies of hydrogen and acceptor defects in rutile TiO2

The behaviour of hydrogen in both defect free and acceptor doped bulk rutile TiO 2 is investigated through defect calculations performed within the density functional theory formalism. Both interstitial and substitutional hydrogen defects are shown to behave as shallow donors in the material, thereby existing as effectively positive hydroxide defects, , and substitutional hydrogen defects, . Of the investigated isolated hydrogen defects, the defect is shown to have the lowest formation energy over the whole Fermi level range under both oxidising and reducing conditions. However, the formation energy of is only 0.35 eV higher under conditions where TiO 2 is in equilibrium with Ti 2 O 3 , indicating that it exists as a minority defect in rutile TiO 2 under highly reducing conditions such as under growth of TiO 2 on a Ti metal surface. The enthalpy of hydration of oxygen vacancies is calculated to be −1.64 and −1.60 eV for the 2 × 2 × 3 and 3 × 3 × 3 supercells, indicating that defects will prevail in wet atmospheres, even at high temperatures. Hydrogen incorporated in the material can furthermore be expected to associate significantly with various acceptor centres ( e.g. , substitutional N and Al acceptors and Ti vacancies). The binding energies of the substitutional NH × O (imide) defect and of the association complexes between H and fully ionised substitutional Al, , and Ti vacancies, and ( i.e. , Ruetschi type defects), are calculated to be −0.36, −0.12, −0.47 and −0.82 eV, respectively. This work presents detailed studies of the thermodynamic stability of H related defects in pure and acceptor doped rutile TiO 2 .