Strength Evaluation of Functionalized MWCNT-Reinforced Polymer Nanocomposites Synthesized Using a 3D Mixing Approach
The incorporation of carboxyl functionalized multi-walled carbon nanotube (MWCNT- COOH) into a polymethyl methacrylate (PMMA) has been investigated. The resultant tensile and flexural mechanical properties have been determined. In this paper, a novel synthesis process for a MWCNT-reinforced polymer...
Gespeichert in:
Veröffentlicht in: | Materials 2022-10, Vol.15 (20), p.7263 |
---|---|
Hauptverfasser: | , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The incorporation of carboxyl functionalized multi-walled carbon nanotube (MWCNT- COOH) into a polymethyl methacrylate (PMMA) has been investigated. The resultant tensile and flexural mechanical properties have been determined. In this paper, a novel synthesis process for a MWCNT-reinforced polymer nanocomposite is proposed. The proposed method significantly eliminates the most challenging issues of the nano-dispersed phase, including agglomeration and non-homogeneous mixing within a given matrix material, and also resolves the issues occurring in conventional mixing processes. The results of scanning electron microscopy support these claims. This 3D-mixing process is followed by an extrusion process, using a twin-screw extruder for pristine MWCNT, and a compression molding process for COOH-MWCNT, to prepare test specimens for experimentally determining the mechanical properties. The test specimens are fabricated using 0.1, 0.5, and 1.0 wt.% MWCNT, with a remaining PMMA phase. The testing is conducted according to ASTM D3039 and ASTM D7264 standards. Significant improvements of 25.41%, 35.85%, and 31.75% in tensile properties and 18.27%, 48%, and 33.33% in flexural properties for 0.1, 0.5, and 1.0 wt.% COOH-MWCNT in PMMA, respectively, compared to non-functionalized MWCNTs, were demonstrated. The highest strength was recorded for the nanocomposite with 0.5 wt.% f-MWCNT content, indicating the best doping effect at a lower concentration of f-MWCNT. The proposed CNT-PMMA nanocomposite may be found suitable for use as a scaffold material in the domain of bone tissue engineering research. This type of research possesses a high strength requirement, which may be fulfilled using MWCNT. Furthermore, this analysis also shows a significant amount of enhancement in flexural strength, which is clinically required for fabricating denture bases. |
---|---|