Evaluation of Thermal Fatigue Life and Crack Morphology in Brake Discs of Low-Alloy Steel for High-Speed Trains

Effective braking in high-speed trains is one of the major bottlenecks in expediting the technology and possibilities to improve speed. Although substantial progress has been made to increase operating speed, perhaps, thermal fatigue cracking in brake discs is a primary constraint so far. Thermal fa...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Materials 2022-10, Vol.15 (19), p.6837
Hauptverfasser: Wang, Jinnan, Chen, Yunbo, Zuo, Lingli, Zhao, Haiyan, Ma, Ninshu
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Effective braking in high-speed trains is one of the major bottlenecks in expediting the technology and possibilities to improve speed. Although substantial progress has been made to increase operating speed, perhaps, thermal fatigue cracking in brake discs is a primary constraint so far. Thermal fatigue cracking is the major cause of brake disc failure in high-speed trains, especially trains with a speed of 350 km/h or above. In this study, new material composition is proposed for brake discs of high-speed trains. A comprehensive investigation is presented based on fatigue crack initiation and propagation, along with wear and micro-hardness characterization. Thermal fatigue tests at various thermal cycles between 20 ℃ and 700 ℃ were performed and the experimental results are compared with fatigue properties of a commercial brake disc material. An experimental trial revealed that thermal cracks normally initiate and propagate along the oxidized grain boundaries; nevertheless, crack propagation is restricted by the fine precipitates and lath structure of martensitic. Moreover, crack length at the initiation and propagation stage is predicted through crack growth rate and favorable grain size in the crack vicinity. Thermal fatigue life can be improved by dictating the microstructure and precipitate morphology of cast steel by tailoring the alloying composition.
ISSN:1996-1944
1996-1944
DOI:10.3390/ma15196837