Novel Nd-N/TiO2 Nanoparticles for Photocatalytic and Antioxidant Applications Using Hydrothermal Approach

In this study, photocatalysis was employed to degrade a wastewater pollutant (AB-29 dye) under visible light irradiation. For this purpose, nitrogen (N)- and neodymium (Nd)-doped TiO2 nanoparticles were prepared using the simple hydrothermal method. X-ray diffraction (XRD) revealed an anatase phase...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Materials 2022-09, Vol.15 (19), p.6658
Hauptverfasser: Alam, Mir Waqas, Khalid, N. R., Naeem, Sumaira, Niaz, N. A., Ahmad Mir, Tanveer, Nahvi, Insha, Souayeh, Basma, Zaidi, Noushi
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this study, photocatalysis was employed to degrade a wastewater pollutant (AB-29 dye) under visible light irradiation. For this purpose, nitrogen (N)- and neodymium (Nd)-doped TiO2 nanoparticles were prepared using the simple hydrothermal method. X-ray diffraction (XRD) revealed an anatase phase structure of the Nd-N/TiO2 photocatalyst, whereas properties including the surface morphology, chemical states/electronics structure and optical structure were determined using transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and UV–visible (UV–vis.) and photoluminescence (PL) spectroscopies. Photocatalytic testing of the prepared nanomaterials was performed to remove acid blue-29 (AB-29) dye under visible-light exposure. The prepared Nd-N/TiO2 nanoparticles demonstrated a superior photocatalytic activity and the decolorization efficiency was about 92% after visible-light illumination for 1 h and 20 min, while N/TiO2, Nd/TiO2 and TiO2 only showed a 67%, 43% and 31% decolorization efficiency, respectively. The enhanced photocatalytic activity of the Nd-N/TiO2 photocatalyst was due to a decrease in the electron/hole’s recombination and the increased absorption of TiO2 in the visible range. The reusability results showed that the average photocatalytic activity decrease for all the samples was only about 16% after five consecutive cycles, indicating a good stability of the prepared nanomaterials. Moreover, the radical scavenging activity of the prepared nanomaterials was evaluated using the DPPH method. The novel Nd-N/TiO2 exhibited a higher antioxidant activity compared to all the other samples.