NiCrBSi Coatings Fabricated on 45 Steel Using Large Spot Laser Cladding

Ni35 coatings were fabricated on 45 steel using a CO2 laser at various parameters. A relatively large spot (10 mm diameter) was adopted, which was beneficial to the coating quality and the cladding efficiency. The cross-sectional geometry, phase constituent, and microstructure of the coatings were investigated. With a lower specific energy, coating height increased, while coating width, melted depth, dilution rate, width to height ratio and contact angle decreased. Ni35 coating primarily consisted of γ-Ni, FeNi3, Ni3B, Cr23C6, and Cr5B3. Dendrites with flower-like, fishbone-like, pearl-like, and column-like morphologies were observed. The fraction of flower-like dendrites increased gradually with the decrease in scanning velocity due to the dendrite growth direction evolution. With the decrease in scanning velocity, the microstructure of the heat-affected zone transformed from martensite to martensite + sorbite and finally sorbite. The maximum microhardness of the Ni35 coating reached 451.8 HV0.2, which was about double that of the substrate (220 HV0.2).