Root canal pre-treatment and adhesive system affect bond strength durability of fiber posts ex vivo

Objectives To investigate the effect of different pre-treatments on the long-term bond strength of fiberglass posts luted either with dual-curing self-etch adhesives and core build-up composites or with a self-adhesive resin (SAR) cement. Materials and methods In total, 180 human root-filled teeth received post-space preparations and three different dentin pre-treatments (PTs): PT1, ethanol (99%); PT2, ethanol-tertiary-butanol-water-solution (AH Plus Cleaner, Dentsply Sirona; York, USA); and PT3, distilled water (control). Five luting systems were used: FU, Futurabond U (Voco; Cuxhaven, Germany); CL, Clearfil DC Bond (Kuraray Noritake; Okayama, Japan); GR, Gradia Core SE Bond (GC Europe NV; Leuven, Belgium); LU, LuxaBond Universal (DMG; Hamburg, Germany); and RX, RelyX Unicem 2 (3M; Minnesota, USA). Roots were cut into six slices (1 mm thick). From each root canal region, three slices were submitted to immediate and three to post-storage push-out testing. The latter were subjected to thermocycling (5–55°C, 6.000 cycles) and stored for six months in saline solution (0.9%, 37°C). Data were analysed using repeated measures ANOVA and chi-square tests (MV±SD). Results Bond strength was significantly affected by material ( p