Solidification/Stabilization of Arsenic-Containing Tailings by Steel Slag-Based Binders with High Efficiency and Low Carbon Footprint

The disposal of nonferrous metal tailings poses a global economic and environmental problem. After employing a clinker-free steel slag-based binder (SSB) for the solidification/stabilization (S/S) of arsenic-containing tailings (AT), the effectiveness, leaching risk, and leaching mechanism of the SSB S/S treated AT (SST) were investigated via the Chinese leaching tests HJ/T299-2007 and HJ557-2010 and the leaching tests series of the multi-process Leaching Environmental Assessment Framework (LEAF). The test results were compared with those of ordinary Portland cement S/S treated AT (PST) and showed that the arsenic (As) curing rates for SST and PST samples were in the range of 96.80–98.89% and 99.52–99.2%, respectively, whereby the leached-As concentration was strongly dependent on the pH of the leachate. The LEAF test results showed that the liquid–solid partitioning limit of As leaching from AT, SST, and PST was controlled by solubility, and the highest concentrations of leached As were 7.56, 0.34, and 0.33 mg/L, respectively. The As leaching mechanism of monolithic SST was controlled by diffusion, and the mean observed diffusion coefficient of 9.35 × 10−15 cm2/s was higher than that of PST (1.55 × 10−16 cm2/s). The findings of this study could facilitate the utilization of SSB in S/S processes, replacing cement to reduce CO2 emissions.